  • Résine PU polyuréthane polyol ISO pour pneu en mousse
  • Résine PU polyuréthane polyol ISO pour pneu en mousse
  • Résine PU polyuréthane polyol ISO pour pneu en mousse
  • Résine PU polyuréthane polyol ISO pour pneu en mousse
  • Résine PU polyuréthane polyol ISO pour pneu en mousse
  • Résine PU polyuréthane polyol ISO pour pneu en mousse

Résine PU polyuréthane polyol ISO pour pneu en mousse

Payment Type:
L/C,T/T,D/P
Incoterm:
FOB,CFR,CIF
Min. Order:
18000 Kilogram
Delivery Time:
10 Days
Transportation:
Ocean
Port:
Shanghai
Share:
  • Description du produit
Overview
Product Attributes

marqueXuchuan Chemical

Supply Ability & Additional Informations

Détails d'emballage20 & 225kg / tambour

transportOcean

Lieu d'origineChine

Code SH39095000

HafenShanghai

Type de paiementL/C,T/T,D/P

IncotermFOB,CFR,CIF

Délai de livraison10 jours

Packaging & Delivery
Selling Units:
Kilogram
Package Type:
20 & 225kg / tambour
Résine PU polyuréthane polyol ISO pour pneu en mousse

Les détails du produit

Application Industrial tyre wheel
Product name Polyurethane
A/B Materials Temperatures(℃) 40~45/38~42
A+C/B Mix ratio (By weight) 100/101~103
Cream Time (s) 8~10
End of Rise Time (s) 60~70
Free Rise Foam Density(g/cm3) 0.24~0.26
Mold Temperature(℃) 45~55
Demold Time(min) 5~7

Characteristic: Good handle, smooth surface

Application: Tire

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

A-3070

Liquid

1000~1400

1.01~1.02

18

B-8280

Yellowish transparent liquid or waxy

800~1200

1.08~1.2

20

Materials preheat

A-3070:  preheated at 50~60 for 6~8 hours.          

B-8280:  preheated at 50~60 for 10~12 hours.

Typical processing parameters & Reaction parameter

Items

A/B Materials Temperatures()

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/101~103

8~10

60~70

0.24~0.26

45~55

5~7

The adding content of C-2 should be 250g±10g/18kg

The adding content of water should be 0~90g/18kg according to the reality

The adding content of hardener should be 0~600g/18kg according to the reality

Physical properties

Items

Molded Density
(g/cm3)

Hardness
(Shore A )

Tensile strength
(MPa)

Elongation
 (%)

Tear Strength
(kN/m)

 

 

 

 

Physical  properties

0.50~0.70

55~68

7.5~9.0

340~450

24~33

 

 

Demold time may be prolonged with the increase of sole thickness.

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


PROFIL DE LA SOCIÉTÉ

PROCESSUS DE PRODUCTION
CERTIFICATION
EMBALLAGE ET EXPÉDITION
FAQ

NOUS CONTACTER

Groupes de Produits : Système de polyuréthane pour semelle de chaussure > Système de polyuréthane pour roue de pneu

Envoyer à ce fournisseur
  • *À:
    Mr. LIU
  • *message:
    Votre message doit comporter de 20 à 8000 caractères

Produits connexes

Accueil

Phone

Info de Compagnie

Demande