Gue d'étanchéité en pierre de résine en polyuréthane pour la semelle de chaussures
Obtenir le dernier prixType de paiement: | L/C,T/T |
Incoterm: | FOB,CIF |
Quantité de commande minimum: | 3 Ton |
transport: | Ocean,Land,Air |
Hafen: | Shanghai |
Type de paiement: | L/C,T/T |
Incoterm: | FOB,CIF |
Quantité de commande minimum: | 3 Ton |
transport: | Ocean,Land,Air |
Hafen: | Shanghai |
Modèle: A-9080W/B-6088
marque: Xuchuan
Lieu D'origine: Chine
Types De: Résine synthétique et plastiques
Application: Outsole, slippers, wedge shoes
Keywords: Lady shoe sole
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Package(kg): 18/20kg
Appearence: liquid
Codes: A-9080W/B-6088
Brand: Xuchuan
Application | shoe sole |
Keywords | Lady shoe sole |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Low Density Shoe System Characteristic |
: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Raw Material Polyester Resin Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
|
Xuchuan Chemical créé en 2007, le capital enregistré des sociétés est de 500 millions de RMB. Les principaux produits sont tous des gammes de polyester polyol, de résine en polyuréthane pour les chaussures, des résines en polyuréthane à base d'eau et sans solvant pour le cuir artificiel, les adhésifs de liaison en polyuréthane et les adhésifs à fonte à chaud en polyuréthane.
Maintenant, Xuchuan a 4 bases de production modernes, la capacité de production a atteint 630 000 tonnes par an, des produits exportés vers 32 pays et régions du monde.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.